Polymeric poly(vinyl alcohol) (PVA)-based composite hydrogels are promising materials with various biomedical applications. However, their mechanical and tribological properties should be tailored for such applications. In this study, we report the fabrication of PVA-gellan gum (GG) composite hydrogels and determine the effect of GG content on their rheological and tribological properties. The rheology tests revealed an enhanced storage (elastic) modulus with increased gellan gum (GG) concentration. The results showed up to 89% enhancement of the elastic modulus of PVA by adding 0.5 wt% gellan gum. This elastic modulus (12.1 ± 0.8 kPa) was very close to that of chondrocyte and its surrounding pericellular matrix (12 ± 1 kPa), rendering them ideal for cartilage regeneration applications. Furthermore, the friction coefficient was reduced by up to 80% by adding GG to PVA, demonstrating the increased elastic modulus improved chance of survival under mechanical shear stresses. Examining PVA/GG at different concentrations of 0.1, 0.3, and 0.5 wt% of GG, we demonstrate that at a load of 5 N, the friction coefficient decreases by increasing the GG concentration. However, at higher loads of 10 and 15 N, a 0.3 wt% concentration was sufficient to significantly reduce the friction coefficient. For PVA and PVA/GG composites, we observed a reduction in friction coefficient by increasing the load from 5 to 15 N. We also found the friction to be independent of the sliding velocity. Possible mechanisms of achieving a reduced friction coefficient are discussed.
Loading....